[Effect of printing orientation on physical and mechanical properties of 3D printing prosthodontic base resin materials].

OBJECTIVE: To analyze the influence of forming direction on the surface characteristics, elastic modulus, bending strength and fracture toughness of printed parts and the relationship between forming direction and force direction, and to provide scientific basis and guidance for the clinical application of oral denture base resin materials. METHODS: The 3D printing technology was used to print denture base resin samples. The shape and size of the samples referred to the current standard for testing conventional denture base materials. The samples used for physical performance testing were cylindrical (with a diameter of 15 mm and a thickness of 1 mm) and printed at different angles along the Z axis (0°, 45°, 90°). Scanning electron microscope was used to observe the microscopic topography of the different samples. The color stability of different samples was observed by color stabilizer. The surface roughness of the samples was analyzed by using surface roughness tester. The Vickers hardness was measured to analyze the hardness of the samples. The samples used for mechanical performance testing were rectangular (elastic modulus and bending strength: A length of 64 mm, a width of 10 mm, and a height of 3.3 mm; fracture toughness: A length of 39 mm, a width of 8 mm, and a height of 4 mm), divided into two groups: W group and H group. The W group was printed from the bottom up along the Z axis with the length × width as the bottom surface parallel to the X, Y axis plane, while the H group printed from the bottom up along the Z axis with the length × height as the bottom surface parallel to the X, Y axis plane. The forming angles of both groups were equally divided into 0°, 45°, and 90°. The elastic modulus, bending strength and fracture toughness of different samples were studied through universal mechanical testing machine. SPSS 22.0 software was used for statistical analysis. RESULTS: The microscopic topography and roughness of different samples were closely related to the printing direction, with significant differences between the 0°, 45°, and 90° specimens. The 0° specimens had the smoothest surface (roughness < 1 µm). The surface of the 45° specimen was the roughest (roughness>3 µm). The microhardness of the 0° sample was the best [(196.13±0.20) MPa], with a significant difference compared with the 90° sample [(186.62±4.81) MPa, P < 0.05]. The mechanical properties of different samples were also closely related to the printing direction. The elastic modulus, bending strength, and fracture toughness of the 45° samples in the W group were the highest compared with the other groups. The results of elastic modulus showed that in the H group, the 45° specimens had the highest elastic mo-dulus, which was significantly different from the 0° and 90° specimens (P < 0.05). The elastic modulus of 0° and 45° specimens in the W group were higher than those in 90° specimens (P < 0.05). The bending strength results showed that there was no significant difference between the specimens from dif-ferent angles in the H group. The bending strength of the 90° specimens in the W group was the smallest, and there was a significant difference between 90° and the 0° and 45° specimens (P < 0.05); And the bendind strength of the 0° and 45° specimens in the W group was significantly higher than that of the 0° and 45° specimens in the H group (P < 0.05). The fracture toughness results showed that the fracture toughness of the H group specimens was lower than 1.9 MPa m1/2, which was specified in the denture base standard. The 45° samples in the W group were the highest, with significant differences compared with the 0° and 90° samples (P < 0.05). And the 90° samples of the W group specimens were lower than 1.9 MPa m1/2. And the fracture toughness of the 45° specimen in the W group was significantly higher than that of all the specimens in the H group (P < 0.05). CONCLUSION: The 0° samples had relatively better physical properties. The 45° samples had the best mechanical properties. But the fracture toughness of specimens (H group and 90° samples of W group) did not yet meet clinical requirements. That indicated that the characteristics of the 3D printing denture base resin were affected by the printing direction. Only when the performance of the printed samples in all directions met the minimum requirements of the standard, they could be used in clinical practice.

Effect of thermal cycling on the flexural strength of 3-D printed, CAD/CAM milled and heat-polymerized denture base materials.

BACKGROUND: This study compared the impact of thermal cycling on the flexural strength of denture-base materials produced through conventional and digital methods, using both subtractive and additive approaches. METHODS: In total, 60 rectangular specimens were fabricated with specific dimensions for flexural strength tests. The dimensions were set according to the International Organization for Standardization (ISO) guideline 20795-1:2013 as 64 × 10 × 3.3 ± 0.2 mm. Specimens from each material group were divided into two subgroups (thermal cycled or nonthermal cycled, n = 10/group). We used distinct methods to produce three different denture-base materials: Ivobase (IB), which is a computer-aided-design/computer-aided-manufacturing-type milled pre-polymerized polymethyl methacrylate resin disc; Formlabs (FL), a 3D-printed denture-base resin; and Meliodent (MD), a conventional heat-polymerized acrylic. Flexural strength tests were performed on half of the samples without a thermal-cycle procedure, and the other half were tested after a thermal cycle. The data were analyzed using a two-way analysis of variance and a post hoc Tukey test (α = 0.05). RESULTS: Based on the results of flexural-strength testing, the ranking was as follows: FL > IB > MD. The effect of thermal aging was statistically significant for the FL and IB bases, but not for the MD base. CONCLUSIONS: Digitally produced denture bases exhibited superior flexural strength compared with conventionally manufactured bases. Although thermal cycling reduced flexural strength in all groups, the decrease was not statistically significant in the heat-polymerized acrylic group.

A 3D-simulation study of the deformation, tension, and stress of 3D-printed and conventional denture base materials after immersion in artificial saliva.

INTRODUCTION: The worldwide application of digital technology has presented dentistry with transformative opportunities. The concept of digital dentures, incorporating computer-aided design (CAD) and computer-aided manufacturing (CAM) techniques, holds the promise of improved precision, customization, and overall patient satisfaction. However, the shift from traditional dentures to their digital counterparts should not be taken lightly, as the intricate interplay between oral physiology, patient comfort, and long-term durability requires thorough examination.

Biomechanical Behavior of a 3D-Printed Denture Base Material.

PURPOSE: To evaluate relevant material properties (flexural strength [σf], elastic modulus [E], water sorption [Wsp] and solubility [Wsl], and biocompatibility) of an additive manufacturing (AM) polymer vs a heat-curing acrylic resin (AR; control) for the manufacture of complete dentures, testing the hypothesis that fabrications from both materials would present acceptable material properties for clinical use. MATERIALS AND METHODS: The σf, E, Wsp, and Wsl were evaluated according to the ISO 20795-1:2013 standard, and the biocompatibility was evaluated using MTT and SRB assays. Disk-shaped specimens were fabricated and used for Wsp (n = 5), Wsl (n = 5), and biocompatibility (n = 3) testing. For assessment of σf and E, bar-shaped specimens (n = 30) were fabricated and stored in 37°C distilled water for 48 hours or 6 months before flexural testing in a universal testing machine with a constant displacement rate (5 ± 1 mm/minute). Data from σf, E, Wsp, Wsl, and biocompatibility tests were statistically analyzed using Student t test (α = .05). Weibull analysis was also used for σf and E data. RESULTS: Significant differences between the two materials were found for the evaluated material properties. Water storage for 6 months did not affect the flexural strength of the AM polymer, but this material showed inadequate σf and Wsl values. CONCLUSIONS: Despite adequate biocompatibility and strength stability after 6 months of water storage, the AM polymer recommended for complete dentures needs further development to improve the material properties evaluated in this study.

Working viscosity and non-Newtonian behavior of silicone denture liners.

PURPOSE: To evaluate flow profile and non-Newtonian behavior of 10 different silicone lining materials. METHODS: Ten commercially available silicone lining materials were selected for evaluation. The flow profile and non-Newtonian behavior of each material was measured using a shark fin testing method. Fin height and resultant base thickness were measured with a digital caliper and compared with one-way ANOVA and Student-Newman-Keuls post hoc test and fin base by Kruskal-Wallis one-way ANOVA on ranks with Dunn post hoc test with significance at P< 0.05 for both. RESULTS: Shark fin heights ranged from 9.62 ± 0.86 mm [Reline II (Soft)] to 25.54 ± 0.43 mm [Sofreliner (Medium)]. Shark fin bases ranged from 2.57 ± 0.51 mm [Sofreliner (Medium)] to 10.31 ± 0.57 mm [Reline II (Soft)]. Statistically significant differences were found between certain samples' shark fin heights as well as resultant bases (P< 0.05) indicating different rheological properties. CLINICAL SIGNIFICANCE: Silicone liner materials differ significantly with respect to flow profile and non-Newtonian behavior. While a high flow profile (low viscosity) of an elastomeric impression material improves accuracy, it may be a detriment to a denture lining material that must achieve a critical minimum thickness to provide resilience. Likewise, a low flow profile (high viscosity) material may also pose a disadvantage, requiring excessive compression and possible tissue distortion to achieve the same critical thickness. The results of this study should be considered when selecting the appropriate material for clinical application. Additional studies are indicated to further quantify rheological properties as well as correlate them to physical properties after the complete cure of the material.

Flexural strength of repaired denture base materials manufactured for the CAD-CAM technique.

PURPOSE: To evaluate the flexural properties of repaired poly(methylmethacrylate) (PMMA) denture base materials for computer-aided design/computer-aided manufacturing (CAD-CAM) and to compare them with heat-activated polymerized PMMA. METHODS: A total of 288 specimens (65 × 10 × 2.5 mm) were prepared using both CAD-CAM and conventional blocks and repaired using autopolymerizing and visible-light polymerizing (VLC) materials. Microwave energy, water storage and hydroflask polymerization were applied as additional post-polymerization cycles after the repair process. The flexural strength (FS) of the specimens was evaluated using the three-point bending test. Data were evaluated statistically using 2-way ANOVA followed by Bonferroni's correction to determine the significance of differences between the groups (P ≤ 0.05). RESULTS: The FS of the denture base materials for CAD-CAM was significantly higher than that for the heat-activated group (P ≤ 0.05). The FS was significantly highest when microwave energy was used for the post-polymerization cycle. The FS values for all groups repaired with VLC resin were significantly lower than for the autopolymerization group (P ≤ 0.05). CONCLUSION: The flexural properties of denture base materials for CAD-CAM repaired using autopolymerizing acrylic resins can recover by 50-70%. Additional post-polymerization cycles for autopolymerizing repair resin can be suggested to improve the clinical service properties of repaired dentures.

Biofilm removal effect of diatom complex on 3D printed denture base resin.

For patients who have difficulty in mechanical cleaning of dental appliances, a denture cleaner that can remove biofilm with dense extracellular polymeric substances is needed. The purpose of this study is to evaluate the efficacy of diatom complex with active micro-locomotion for removing biofilms from 3D printed dentures. The diatom complex, which is made by doping MnO2 nanosheets on diatom biosilica, is mixed with H2O2 to generate fine air bubbles continuously. Denture base resin specimens were 3D printed in a roof shape, and Pseudomonas aeruginosa (107 CFU/mL) was cultured on those for biofilm formation. Cleaning solutions of phosphate-buffered saline (negative control, NC), 3% H2O2 with peracetic acid (positive control, PC), denture cleanser tablet (DCT), 3% H2O2 with 2 mg/mL diatom complex M (Melosira, DM), 3% H2O2 with 2 mg/mL diatom complex A (Aulacoseira, DA), and DCT with 2 mg/mL DM were prepared and applied. To assess the efficacy of biofilm removal quantitatively, absorbance after cleaning was measured. To evaluate the stability of long-term use, surface roughness, ΔE, surface micro-hardness, and flexural strength of the 3D printed dentures were measured before and after cleaning. Cytotoxicity was evaluated using Cell Counting Kit-8. All statistical analyses were conducted using SPSS for Windows with one-way ANOVA, followed by Scheffe's test as a post hoc (p < 0.05). The group treated with 3% H2O2 with DA demonstrated the lowest absorbance value, followed by the groups treated with 3% H2O2 with DM, PC, DCT, DCT + DM, and finally NC. As a result of Scheffe's test to evaluate the significance of difference between the mean values of each group, statistically significant differences were shown in all groups based on the NC group. The DA and DM groups showed the largest mean difference though there was no significant difference between the two groups. Regarding the evaluation of physical and mechanical properties of the denture base resin, no statistically significant differences were observed before and after cleaning. In the cytotoxicity test, the relative cell count was over 70%, reflecting an absence of cytotoxicity. The diatom complex utilizing active micro-locomotion has effective biofilm removal ability and has a minimal effect in physical and mechanical properties of the substrate with no cytotoxicity.

Anti-Microbial Effect of AgBr-NP@CTMAB on Streptococcus Mutans and Assessment of Surface Roughness Hardness and Flexural Strength of PMMA.

Purpose: To investigate the inhibition of Streptococcus mutans (S.mutans) and its biofilm by AgBr-nanoparticles (NP) @CTMAB (cetyltrimethyl-ammonium bromide) and evaluate the changes in Polymethyl methacrylate (PMMA)'s surface roughness (Ra), microhardness, and flexural strength during prolonged immersion in AgBr-NP@CTMAB for application in the denture cleaning industry. Patients and Methods: The antibacterial activity of AgBr-NP@CTMAB against S.mutans was measured colony formation assay, OD600 and laser confocal microscopy. Changes in the specimens' values for surface roughness, microhardness, and flexural strength (MPa) were measured after immersion solutions for 180 or 360 days. Results: The AgBr-NP@CTMAB solution exhibited a robust antibacterial effect on planktonic S. mutans, with a minimum bactericidal concentration of 5 µg/mL. The 10 µg/mL AgBr-NP@CTMAB solution efficiently inhibited S. mutans biofilm formation. (2) No significant difference in surface roughness after immersion in AgBr-NP@CTMAB (10 µg/mL and 20 µg/mL) comparing with distilled water (P > 0.05) and Polident had significantly higher than distilled water (P < 0.05). There was a significant decrease in the surface hardness of the PMMA specimens that were immersed in the Polident compared with those in distilled water (P < 0.05). While, no significant differences in surface hardness after immersion in the AgBr-NP@CTMAB (P > 0.05). The result of flexural strength suggested that there was no statistically significant difference (P < 0.05) between AgBr-NP@CTMAB as well as Polident and water. Conclusion: AgBrNP@CTMAB can efficiently inhibit the growth of plankton S.mutans and biofilm formation, without affecting the flexural strength, microhardness, or surface roughness of PMMA. Therefore, AgBrNP@CTMAB holds promise as a new denture cleaning agent.

Evaluation and assessment of the wettabilty and water contact angle of modified poly methyl methacrylate denture base materials against PEEK in cast partial denture framework: an in vitro study.

INTRODUCTION: The prevalence of adults with partially dental arches is expected to be more than imagined and patients requiring replacement of missing teeth are slowly increasing in number too. Removable partial dentures are known to provide for substantial replacement for the missing teeth with also added advantages when compared to fixed or implant prosthesis, mainly in elderly patients. Denture base material performance and durability are greatly influenced by wettability and water contact angle. In the case of dentures; adequate moisture distribution is necessary to ensure excellent wettability which has an influence on comfort and oral health. The purpose of conducting this study was to find out whether the advancements made using PEEK (Polyether ether ketone) would prove to be more beneficial than the current upgrades in the current material spectrum. MATERIALS AND METHODS: This study was performed under in vitro conditions. All the fabrication and processing was done only by one operator. The materials used were divided into three groups each comprising 20 samples. Group A was modified polymethylmethacrylate (Bredent Polyan), Group B was polyoxymethylene acetal resin (Biodentaplast) and Group C was PEEK. An Ossila Goniometer was used to measure the contact angle. The three types of liquids used for the testing included distilled water, natural saliva and mouth wetting solution (Wet Mouth Liquid, ICPA India). Human saliva was collected from an individual with no medical conditions and normal salivary secretion. RESULTS: The data was analyzed using One-way ANOVA test and a pairwise comparison using the Post Hoc Tukey's Honest Significant Difference. Table 1 consists of the mean water contact angles of the denture base materials and mean contact angles of various denture base materials. In saliva, mouth wetting solution and distilled water, the highest mean and least mean contact angle was seen in Polyan and Biodentaplast respectively. A signicant difference was seen between PEEK and Polyan and Biodentaplast and Polyan on further comparison. CONCLUSION: From the resources and the materials at our disposal, it could be concluded that Polyan, Biodentaplast and PEEK and could be used as viable options in cast partial denture framework.

[Effect of Aging on the Mechanical Properties of CAD/CAM-Milled and 3D-Printed Acrylic Resins for Denture Bases].

PURPOSE: The purpose of this study was to investigate the mechanical properties of acrylic resins at different aging times for denture bases manufactured using the conventional method, microwave processing, milling, and 3D printing. MATERIALS AND METHODS: A total of 160 rectangular samples (64 Å~ 10 Å~ 3.3 ± 0.03 mm) were prepared, divided among the four main resin groups, and subdivided into four analysis times (T0, T1, T2, and T3), resulting in 10 samples per subgroup. The samples were stored in distilled water at 37° ± 2°C for 24 hours (T0), then subjected to thermocycling at temperatures of 5° ± 1°C and 55° ± 1°C in different numbers of cycles: 5,000 (T1); 10,000 (T2); and 20,000 (T3). The mechanical properties evaluated were surface microhardness, flexural strength, and modulus of elasticity. Statistical differences between resin groups and aging time were evaluated using two-way analysis of variance (P < .05). RESULTS: The 3D-printed resin showed the significantly lowest values of microhardness, flexural strength, and modulus of elasticity compared to other resins (P < .001). CONCLUSIONS: The CAD/CAM-milled denture resin showed mechanical properties similar to those of traditional resins (conventional and microwave-processed). The 3D-printing resin did not show adequate mechanical properties for long-term clinical use. Despite this, new studies are developing better properties of this resin for long-term use.

Effect of thermocycling on surface topography and fracture toughness of milled and additively manufactured denture base materials: an in-vitro study.

BACKGROUND: Studies investigating thermocycling effect on surface topography and fracture toughness of resins used in digitally manufactured denture bases are few. The study aimed to assess the impact of thermocycling on surface topography and fracture toughness of materials used for digitally manufactured denture bases. METHODS: Water sorption, solubility, hardness, surface roughness, and fracture toughness of both three-dimensional (3D)-printed and computer-aided design, computer-aided manufacturing (CAD-CAM) milled specimens (n = 50) were assessed both prior to and following 2000 thermocycles, simulating 2 years of clinical aging. Surface hardness (n = 10) was measured using a Vickers hardness testing machine, surface roughness (n = 10) was determined by a contact profilometer, and fracture toughness (n = 20) was measured using the 3-point bend test, then studying the fractured surfaces was done via a scanning electron microscope (SEM). Prior to and following thermocycling, water sorption and solubility (n = 10) were assessed. Normally distributed data was tested using two-way repeated ANOVA and two-way ANOVA, while Mann Whitney U test and the Wilcoxon signed ranks test were used to analyze data that was not normally distributed (α < 0.05). RESULTS: Following thermocycling, Vickers hardness and fracture toughness of both groups declined, with a significant reduction in values of the 3D-printed resin (P < .001). The 3D-printed denture base resins had a rougher surface following thermocycling with a significant difference (P < .001). The sorption and solubility of water of both materials were not affected by thermocycling. CONCLUSIONS: Before and after thermocycling, milled specimens had lower surface roughness and a greater degree of hardness and fracture toughness than 3D-printed specimens. Thermocycling lowered hardness and fracture toughness, and increased surface roughness in both groups, but had no effect on water sorption and solubility.

The effect of aging on hardness of heat cured denture base resin modified with recycled acrylic resin.

BACKGROUND: The second rule of the 4Rs concept (Reduce, Reuse, Recycle, and Recover) was applied in this study using recycled acrylic resin to improve the hardness and study the effect of aging on the hardness of heat cured denture base resins. METHOD: Forty heat-cured acrylic resin samples were prepared and divided into control and modified groups. The hardness was tested using a type D durometer hardness tester for evaluating the effect of the thermal aging process on the hardness in the control and modified groups. The samples were either subjected to thermal aging (the specimens thermo-cycled 10 cycles per day between 55°C and 5°C with a 30-s dwell time) or were not. RESULTS: The mean difference in hardness between specimens with and without aging in the modified group increased with increasing concentrations of incorporated recycled acrylic resin. Independent samples t test revealed that the hardness values of modified groups with aging were significantly higher than in those without aging (p ≤ 0.05). ANOVA revealed that the modified group revealed a significant increase in hardness than that of the control group (p ≤ 0.05). CONCLUSIONS: Recycling and reuse of acrylic resins improved the hardness of denture base resins. The aging period significantly affected the hardness values of the control and modified groups.

Trueness of artificial teeth for CAD-CAM complete dentures fabricated with additive manufacturing implementing different denture base-tooth offset values: An in vitro study.

STATEMENT OF PROBLEM: Computer-aided design and computer-aided manufacturing (CAD-CAM) removable dentures have become popular. However, evaluations of the effect of denture base-tooth offset (DTO) values on the trueness of artificial teeth are lacking. PURPOSE: The purpose of this in vitro study was to digitally measure the trueness of the artificial teeth of CAD-CAM dentures fabricated with additive manufacturing using different DTO values and to determine the most accurate DTO value. MATERIAL AND METHODS: Seven study groups were formulated based on different DTO values, and 6 maxillary complete dentures were assigned to each group (n=42). A design software program was used to export the monoblock denture as control, the artificial teeth, and 7 different designs of denture bases with DTO values of 0.00, 0.01, 0.03, 0.05, 0.10, 0.15, and 0.20 mm. Denture bases were printed in denture base resin (Denture base RP; formlabs), artificial teeth were printed in tooth-shade resin (Denture teeth A2; formlabs), and both were then assembled and polymerized together. The dentures were scanned (InEos X5; Dentsply Sirona), scan data were imported in a measuring software program (GOM Inspect; GOM GmbH), and registration using local best fit was performed to align data. Color-coded maps for the surface comparison of each denture with the control denture scan were generated. Fitting center points were constructed for each artificial tooth, which were compared with their corresponding points on the data of the control scan. Multiple pairwise comparisons were performed after 1-way ANOVA to quantify and statistically evaluate the deviation values (α=.05). RESULTS: The 0.10-mm DTO group showed the lowest values when comparing artificial tooth deviations both individually and as types. On comparing the average deviations, statistically significant differences were identified among the 7 groups (P<.001). A nonstatistically significant difference was identified when the 0.10- and 0.05-mm DTO groups were compared. Lower deviation values were found in the premolars compared with the molars, in the incisors compared with the canines, and in posterior artificial teeth compared with anterior teeth. CONCLUSIONS: The 0.10-mm DTO value showed the highest trueness for the artificial teeth compared with the other DTO values tested in this study. The 0.05-mm DTO value is an alternative to the 0.10-mm DTO value for CAD-CAM dentures constructed by additive manufacturing. Anterior teeth of a CAD-CAM denture showed higher deviation values compared with posterior teeth.

Effect of post-curing conditions on surface characteristics, physico-mechanical properties, and cytotoxicity of a 3D-printed denture base polymer.

OBJECTIVE: This study aims to investigate the influence of post-polymerization (post-curing) conditions on surface characteristics, flexural properties, water sorption and solubility, and cytotoxicity of additively manufactured denture base materials. METHODS: The tested specimens were additively manufactured using digital light processing and classified into different post-curing condition groups: submerged in water (WAT), submerged in glycerin (GLY), and air exposure (AIR). An uncured specimen (UNC) was used as a control. The surface topography and roughness were observed. The flexural strength and modulus were determined via a three-point bending test. The water sorption and solubility were subsequently tested. Finally, an extract test was performed to assess cytotoxicity. RESULTS: Different post-curing conditions had no significant effects on the surface topography and roughness (Sa value). Various post-curing conditions also had no significant effects on the flexural strength. Notably, the flexural modulus of the WAT group (2671.80 ± 139.42 MPa) was significantly higher than the AIR group (2197.47 ± 197.93 MPa, p = 0.0103). After different post-curing conditions, the water sorption and solubility of the specimens met the ISO standards. Finally, all post-curing conditions effectively reduced cytotoxic effects. SIGNIFICANCES: Post-curing with different oxygen levels improved flexural properties, and flexural modulus significantly increased after the specimens were submerged in water. In addition, water sorption and solubility, and cytocompatibility were optimized by post-curing, irrespective of the post-curing conditions. Therefore, the water-submerged conditions optimized the flexural modulus of the 3D-printed denture base materials.

Evaluation of flexural strength, impact strength, and surface microhardness of self-cured acrylic resin reinforced with silver-doped carbon nanotubes.

BACKGROUND: Poly-methyl methacrylate (PMMA) is a type of polymer mostly used to make denture bases. Self-cured acrylic resin (PMMA) can be used to repair a fractured acrylic denture base; however, even after repair, this area remains vulnerable. Carbon nanotubes (CNTs) could be used as a filler for polymer reinforcement. Furthermore, silver nanoparticles are efficient agents for the prevention of dental biofilm and improving their mechanical properties. The doping of CNTs with silver nanoparticles may lead to a synergistic interaction that is predicted to enhance the mechanical characteristics of the fillers. OBJECTIVES: The aim of the study was to assess the influnce of manual incorporation of 0.5% weight percent (%wt.) of silver doped carbon nanotubes (Ag-doped CNTs) into commercial self-cured PMMA on its flexural strength, impact strength, and surface microhardness. METHODS: In this investigation, a total of 60 specimens comprised of acrylic resin were employed. They are divided into two main groups: (a) the control group, which was made by using liquid monomer and commercial self-cured PMMA powder; and (b) the modified group, prepared by hand mixing the purchased silver-doped CNTs powder (0.5% wt.) to self-cured PMMA powder (99.5%wt.), and then the blended powder was incorporated into the liquid monomer. Flexural strength, flexural modulus, impact strength, and surface microhardness were evaluated. Independent sample t-tests were used to statistically analyze the data and compare the mean values of flexural strength, flexural modulus, impact strength, and surface microhardness (p-value ≤ 0.05). RESULTS: The flexural strength of the modified groups with Ag-doped CNTs (132.4 MPa) was significantly greater than that of the unmodified (control) groups (63.2 MPa). Moreover, the flexural modulus of the modified groups with Ag-doped CNTs (3.067 GPa) was significantly greater than that of the control groups (1.47 GPa). Furthermore, the impact strength of the modified groups with Ag-doped CNTs (11.2 kJ/mm2) was significantly greater than that of the control groups (2.3 kJ/mm2). Furthermore, the microhardness of the modified groups with Ag-doped CNTs (29.7 VHN) was significantly greater than that of the control groups (16.4 VHN), (p-value = 0.0001). CONCLUSION: The incorporation of 0.5% wt. silver doped CNTs fillers to the self-cured acrylic resin enhanced its flexural strength, flexural modulus, impact strength, and surface microhardness.

Fracture toughness, work of fracture, flexural strength and elastic modulus of 3D-printed denture base resins in two measurement environments after artificial aging.

OBJECTIVES: To investigate the fracture toughness (KIC), work of fracture (WOF), flexural strength (FS) and elastic modulus (E) of four additively manufactured denture base resins in two different measurement environments after artificial aging. METHODS: Rectangular specimens in two different dimensions (n = 480) were 3D-printed with four denture base resins: Denture 3D+ (DEN; NextDent), Fotodent Denture (FOT; Dreve ProDiMed), Freeprint Denture (FRE; Detax), V-Print dentbase (VPR; VOCO)). KIC, WOF, FS and E were measured after (1) water-storage (37 °C; KIC = 7 d; FS = 50 h); (2) water-storage + hydrothermal-aging (20 min, 0.2 MPa, 134 °C); (3) water storage + thermocycling (10,000 cycles, 5/55 °C) in two measurement environments (i) air-23 °C and (ii) water-37 °C. For FS, fracture types were classified, and relative frequencies determined. Univariate ANOVA, Kruskal-Wallis, Mann-Whitney U, and Spearman's correlation were calculated (p < 0.05, SPSS V.27.0). Weibull modulus (m) was calculated using the maximum likelihood estimation method. RESULTS: DEN showed the highest KIC (5/6 groups), WOF and highest corresponding m (1/6 groups), while FRE presented the highest FS (2/6 groups) and E values. Hydrothermal-aging and thermocycling reduced KIC and WOF, FS and E, and the number of FS fracture pieces. For 6/8 groups, hydrothermal aging resulted in lower FS than thermocycling. Measurement in air-23 °C led to higher FS for 7/12 groups and a more brittle fracture behavior. A positive correlation between KIC and FS was observed. SIGNIFICANCE: With measurements in air-23 °C resulting in higher FS than reported in water-37 °C, the measurement environment should be adapted to the clinical situation to allow valid predictions on the mechanical behavior of denture base resins when in situ.

Preparation of arginine-loaded mesoporous silica nanoparticles (Arg@MSNs) to improve the mechanical and antibacterial properties of denture base resin.

STATEMENT OF PROBLEM: Whether the incorporation of arginine-loaded mesoporous silica nanoparticles (Arg@MSNs) into denture base resin can improve the mechanical and antibacterial properties is unclear. PURPOSE: The purpose of this in vitro study was to synthesis Arg@MSNs and explore how Arg@MSNs incorporation affects the mechanical and antibacterial properties of denture base resin. MATERIAL AND METHODS: Arg@MSNs were synthesized via a sol-gel process and characterized by transmission electron microscopy (TEM), dynamic light scattering (DLS), and X-ray diffraction (XRD). The prepared Arg@MSNs at different weight ratio concentrations were added into denture base resin as the experimental group, and unmodified denture base resin was the control. The fracture surface and arginine release behavior of each specimen were detected using scanning electron microscopy (SEM) and ultra-high-performance liquid chromatography-tandem mass spectrometer (UHPLC-HESI-MS/MS), respectively. Three-point bend tests were applied using a universal testing machine for evaluation of the mechanical properties of each group (n=5). Antibacterial efficiency (n=3) was evaluated by both quantitative and qualitative analysis using Streptococcus mutans. The cytotoxic effect of the Arg@MSN-modified denture base resin was investigated using a cell counting kit (CCK)-8 test. Data were subjected to 1-way analysis of variance followed by the post hoc Tukey honestly significant difference test (ɑ=.05). RESULTS: The prepared Arg@MSNs had good monodispersity and spherical morphology. Arg@MSN concentration at 0.5 wt%, 1 wt%, and 2.5 wt% resulted in enhanced mechanical properties, while those at 5 wt% were adversely impacted. Biofilm pH values increased with the incorporation of Arg@MSNs, and the antibacterial performance was improved. The CCK-8 test revealed that all formulations were not cytotoxic. CONCLUSIONS: The addition of Arg@MSNs into denture base resin can enhance its mechanical properties and improve its antibacterial performance without any apparent cytotoxic effect.

Effect of immersion in disinfectants on the color stability of denture base resins and artificial teeth obtained by 3D printing.

PURPOSE: To evaluate the effect of immersion in disinfecting solutions on the color stability of denture base resins and artificial teeth obtained by 3D printing. MATERIALS AND METHODS: Forty discs (15 × 3 mm) were obtained for each group: Lucitone 550 and Cosmos Denture 3D (denture base resins), Duralay and Cosmos TEMP 3D (artificial teeth resins). The discs were immersed in disinfectant solutions: Corega Tabs, 2% chlorhexidine digluconate, 0.25% sodium hypochlorite, and distilled water. Color measurements were obtained with a spectrophotometer before immersion in disinfectants and after the simulated periods of 6 and 12 months. Data (ΔE00 ) were submitted to mixed three-way ANOVA and Bonferroni post-test. RESULTS: For denture base resins, Cosmos Denture 3D showed greater color change regardless of the solution and immersion time. The immersion time of 6 months influenced the color change of the denture base resins regardless of the disinfectant solution. For the artificial teeth resins, the immersion time of 12 months showed a significant color change when compared to 6 months. Cosmos TEMP 3D showed greater color change for all solutions, except for 0.25% sodium hypochlorite. Duralay resin showed greater color change in 2% chlorhexidine, regardless of immersion time. CONCLUSIONS: For denture base resins, the immersion time significantly changed the color regardless of the solution. For artificial teeth resins, Cosmos TEMP 3D showed greater color changes in all solutions when compared to Duralay, except for 0.25% sodium hypochlorite. Chlorhexidine digluconate significantly changed the color of Duralay.

Effect of coffee thermocycling on the surface roughness and stainability of denture base materials with different chemical compositions manufactured with additive and subtractive technologies.

OBJECTIVE: To evaluate the effect of coffee thermocycling (CTC) on the surface roughness (Ra ) and stainability of denture base materials with different chemical compositions fabricated by using additive and subtractive manufacturing. MATERIALS AND METHODS: Disk-shaped specimens were additively (FREEPRINT denture, AM) or subtractively (G-CAM, GSM and M-PM, SM) fabricated from three pink denture base materials in different chemical compositions (n = 10). Ra was measured before and after polishing, while color coordinates were measured after polishing. Specimens were subjected to CTC (5000 cycles) and measurements were repeated. Color differences (ΔE00 ) after CTC were calculated. Ra among different time intervals within materials was evaluated by using repeated measures analysis of variance (ANOVA), while 1-way ANOVA was used to evaluate the Ra of different materials within each time interval and the ΔE00 values. Color coordinates within each material were compared by using paired samples t-tests (α = 0.05). RESULTS: Ra before polishing was the highest for all materials (p < 0.001), while SM had its lowest Ra after CTC and AM had its lowest Ra after polishing (p ≤ 0.008). Before polishing, AM had the highest Ra among the materials (p < 0.001). After polishing, SM had higher Ra than AM (p < 0.001). After CTC, GSM had the lowest Ra (p ≤ 0.048). SM had the lowest (p ≤ 0.031) and AM had the highest (p < 0.001) ΔE00 . CTC decreased the a* and b* values of SM and AM (p ≤ 0.017), and increased the L* values of AM (p < 0.001). CONCLUSIONS: Polishing significantly reduced the surface roughness of all materials. CTC did not increase the surface roughness of materials above the clinically acceptable threshold. Only AM had perceptible color change when previously reported threshold values for denture base materials were considered. CLINICAL SIGNIFICANCE: Tested denture base materials may have similar surface stability after coffee thermocycling. However, subtractively manufactured denture base materials may have improved color stability when subjected to long-term coffee consumption.